鋁板大家應該已經不算陌生了，畢竟在我們日常生活中到處可以看到鋁板的身影，今天無錫鋁板廠家的小編進來為大家分享一些避免鋁板在生產過程中被劃傷的注意事項。鋁板是在鋁板加工過程中添加各種合金元素(主要合金元素為銅、硅、鎂、鋅、錳、鎳、鐵、鈦、鉻、鋰等)，以提高鋁板的機械性能和化學指標。合金鋁板具有純鋁板所不具備的一些特殊性能，廣泛應用于船舶、冰箱、模具、航天設備等特殊環境中。

Aluminum plates are no longer unfamiliar to everyone, as they can be seen everywhere in our daily lives. Today, the editor from Wuxi aluminum plate manufacturer will share with you some precautions to avoid scratches on aluminum plates during the production process. Aluminum plate is made by adding various alloy elements (mainly copper, silicon, magnesium, zinc, manganese, nickel, iron, titanium, chromium, lithium, etc.) during the processing of aluminum plate to improve its mechanical properties and chemical indicators. Alloy aluminum plates have some special properties that pure aluminum plates do not possess, and are widely used in special environments such as ships, refrigerators, molds, aerospace equipment, etc.

合金鋁板在生產加工過程中，很容易出現各種疤痕。線條。疤痕的原因有很多。需要多方面注意

Alloy aluminum plates are prone to various scars during the production and processing process. Lines. There are many reasons for scars. Attention needs to be paid to multiple aspects

鋁板表面劃傷的原因。

The reason for scratches on the surface of the aluminum plate.

劃傷.擦傷.碰傷。

Scratches, abrasions, and bumps.

合金鋁板在生產過程中，這些偏析浮出物或硬工業鋁型材顆粒附著在工作帶表面或損壞工作帶，終劃傷型材表面。

During the production process of alloy aluminum sheets, these segregation floats or hard industrial aluminum profile particles adhere to or damage the surface of the work strip, ultimately scratching the surface of the profile.

合金鋁板模具或工作帶上有雜物，模具工作帶硬度較低，使工作帶表面在擠壓時劃傷鋁板

There are debris on the alloy aluminum plate mold or work strip, and the hardness of the mold work strip is low, causing scratches on the aluminum plate surface during extrusion

在出料軌道或床上有裸露的鋁或石墨條，當與鋁接觸時，會劃傷合金鋁板表面

There are exposed aluminum or graphite strips on the discharge track or bed, which can scratch the surface of the alloy aluminum plate when in contact with aluminum

在床上人為拖動合金鋁板造成擦傷

Scratches caused by manually dragging alloy aluminum plates on the bed

合金鋁板在運輸過程中相互摩擦或擠壓，造成損壞。

Alloy aluminum plates may cause damage due to friction or compression during transportation.

解決鋁板表面劃傷的辦法。

A solution to scratches on the surface of aluminum plates.

合金鋁板模具上的工作帶需要打磨光滑，擠壓模具的空刀是否足夠，表面是否光滑。

The working strip on the alloy aluminum plate mold needs to be polished smooth, whether the empty blade of the extrusion mold is sufficient, and whether the surface is smooth.

在生產合金鋁板的過程中，注意模具線的產生。一旦產生線條，需要及時下模停止生產。

During the production of alloy aluminum plates, pay attention to the generation of mold lines. Once a line is produced, it is necessary to immediately stop production by lowering the mold.

在鋁板鋸切過程中：每次鋸切都要及時清理鋸切鋸末。防止二次劃傷。

During the aluminum plate sawing process, it is necessary to clean the sawdust in a timely manner every time it is sawed. Prevent secondary scratches.

同樣，在數控加工鋁板的過程中，還需要防止夾具上殘留的鋁渣劃傷。

Similarly, in the process of CNC machining aluminum plates, it is also necessary to prevent scratches from residual aluminum slag on the fixture.

在出料軌道或床上有裸露的工業鋁型材或石墨條，應避免硬雜物與鋁板接觸時劃傷鋁板表面

Exposed industrial aluminum profiles or graphite strips on the discharge track or bed should be avoided from scratching the surface of the aluminum plate when hard debris comes into contact with the aluminum plate

在生產搬運過程中要輕輕放置，盡量避免隨意拖動或翻轉合金鋁板

During the production and transportation process, it is important to place the alloy aluminum plate gently and avoid dragging or flipping it randomly as much as possible

合理放置鋁板，盡量避免相互摩擦。

Reasonably place aluminum plates and try to avoid friction with each other.

感謝您的閱讀，此文的文章來源：鋁板生產廠家更多的內容和問題請點擊：http://m.ganyuedu.com我們會繼續努力的為您提供服務，感謝您的支持！

Thank you for reading. The source of this article is aluminum plate manufacturers. For more information and questions, please click: http://m.ganyuedu.com We will continue to work hard to provide you with services. Thank you for your support!